Vidal, E., Buxadera-Palomero, J., Pierre, C., Manero, J. M., Ginebra, M. P., Cazalbou, S., Combes, C., Rupérez, E., Rodríguez, D., (2019). Single-step pulsed electrodeposition of calcium phosphate coatings on titanium for drug delivery Surface and Coatings Technology 358, 266-275

Metallic implants have some limitations related to bioactivity and bacteria colonization leading to infections. In this regard, calcium phosphate coatings can be used as carrier for drug delivery in order to improve the mentioned drawbacks. The present work proposes the introduction of an antibacterial agent in the course of a pulsed and reverse pulsed electrodeposition. Calcium phosphate coatings were prepared in 30 min using different pulse waveforms (unipolar-bipolar), current densities (2–5 mA/cm2) and temperatures (40–60 °C). Mechanical stability of the as-coated surfaces was studied in order to select the optimal electrodeposition conditions. Subsequently, selected coatings were loaded with an antiseptic agent, chlorhexidine digluconate (CHX), via a single-step co-deposition procedure. CHX concentration added to the electrolyte was adjusted to 3 mM based on the antibacterial efficacy of the loaded coatings evaluated in vitro with Staphylococcus aureus and Escherichia coli bacteria strains. Whereas the same chlorhexidine concentration was added to the electrolyte, results showed that the amount of CHX loaded was different for each condition while release kinetics was maintained. The results of this work demonstrate that a pulsed co-deposition strategy has great potential to modulate local delivery of antibacterial agents such as chlorhexidine digluconate, which may prevent early phase infections of metallic implants after insertion.

Keywords: Antibacterial agent, Calcium phosphate, Characterization, Coating, Pulse electrodeposition, Titanium


Vidal, E., Buxadera-Palomero, J., Pierre, C., Manero, J. M., Ginebra, M. P., Cazalbou, S., Combes, C., Rupérez, E., Rodríguez, D., (2019). Single-step pulsed electrodeposition of calcium phosphate coatings on titanium for drug delivery Surface and Coatings Technology 358, 266-275

Metallic implants have some limitations related to bioactivity and bacteria colonization leading to infections. In this regard, calcium phosphate coatings can be used as carrier for drug delivery in order to improve the mentioned drawbacks. The present work proposes the introduction of an antibacterial agent in the course of a pulsed and reverse pulsed electrodeposition. Calcium phosphate coatings were prepared in 30 min using different pulse waveforms (unipolar-bipolar), current densities (2–5 mA/cm2) and temperatures (40–60 °C). Mechanical stability of the as-coated surfaces was studied in order to select the optimal electrodeposition conditions. Subsequently, selected coatings were loaded with an antiseptic agent, chlorhexidine digluconate (CHX), via a single-step co-deposition procedure. CHX concentration added to the electrolyte was adjusted to 3 mM based on the antibacterial efficacy of the loaded coatings evaluated in vitro with Staphylococcus aureus and Escherichia coli bacteria strains. Whereas the same chlorhexidine concentration was added to the electrolyte, results showed that the amount of CHX loaded was different for each condition while release kinetics was maintained. The results of this work demonstrate that a pulsed co-deposition strategy has great potential to modulate local delivery of antibacterial agents such as chlorhexidine digluconate, which may prevent early phase infections of metallic implants after insertion.

Keywords: Antibacterial agent, Calcium phosphate, Characterization, Coating, Pulse electrodeposition, Titanium


Sebastian, P., Giannotti, M. I., Gómez, E., Feliu, J. M., (2018). Surface sensitive nickel electrodeposition in deep eutectic solvent ACS Applied Energy Materials , 1, (3), 1016-1028

The first steps of nickel electrodeposition in a deep eutectic solvent (DES) are analyzed in detail. Several substrates from glassy carbon to Pt(111) were investigated pointing out the surface sensitivity of the nucleation and growth mechanism. For that, cyclic voltammetry and chronoamperometry, in combination with scanning electron microscopy (SEM), were employed. X-ray diffraction (XRD) and atomic force microscopy (AFM) were used to more deeply analyze the Ni deposition on Pt substrates. In a 0.1 M NiCl2 + DES solution (at 70 °C), the nickel deposition on glassy carbon takes place within the potential limits of the electrode in the blank solution. Although, the electrochemical window of Pt|DES is considerably shorter than on glassy carbon|DES, it was still sufficient for the nickel deposition. On the Pt electrode, the negative potential limit was enlarged while the nickel deposit grew, likely because of the lower catalytic activity of the nickel toward the reduction of the DES. At lower overpotentials, different hydrogenated Ni structures were favored, most likely because of the DES co-reduction on the Pt substrate. Nanometric metallic nickel grains of rounded shape were obtained on any substrate, as evidenced by the FE-SEM. Passivation phenomena, related to the formation of Ni oxide and Ni hydroxylated species, were observed at high applied overpotentials. At low deposited charge, on Pt(111) the AFM measurements showed the formation of rounded nanometric particles of Ni, which rearranged and formed small triangular arrays at sufficiently low applied overpotential. This particle pattern was induced by the (111) orientation and related to surface sensitivity of the nickel deposition in DES. The present work provides deep insights into the Ni electrodeposition mechanism in the selected deep eutectic solvent.

Keywords: AFM, Deep eutectic solvent, Glassy carbon, Nanostructures, Nickel electrodeposition, Platinum electrode, Pt(111), SEM, Surface sensitive


Sebastian, P., Giannotti, M. I., Gómez, E., Feliu, J. M., (2018). Surface Sensitive Nickel Electrodeposition in Deep Eutectic Solvent ACS Applied Energy Materials , Article ASAP

The first steps of nickel electrodeposition in a deep eutectic solvent (DES) are analyzed in detail. Several substrates from glassy carbon to Pt(111) were investigated pointing out the surface sensitivity of the nucleation and growth mechanism. For that, cyclic voltammetry and chronoamperometry, in combination with scanning electron microscopy (SEM), were employed. X-ray diffraction (XRD) and atomic force microscopy (AFM) were used to more deeply analyze the Ni deposition on Pt substrates. In a 0.1 M NiCl2 + DES solution (at 70 °C), the nickel deposition on glassy carbon takes place within the potential limits of the electrode in the blank solution. Although, the electrochemical window of Pt|DES is considerably shorter than on glassy carbon|DES, it was still sufficient for the nickel deposition. On the Pt electrode, the negative potential limit was enlarged while the nickel deposit grew, likely because of the lower catalytic activity of the nickel toward the reduction of the DES. At lower overpotentials, different hydrogenated Ni structures were favored, most likely because of the DES co-reduction on the Pt substrate. Nanometric metallic nickel grains of rounded shape were obtained on any substrate, as evidenced by the FE-SEM. Passivation phenomena, related to the formation of Ni oxide and Ni hydroxylated species, were observed at high applied overpotentials. At low deposited charge, on Pt(111) the AFM measurements showed the formation of rounded nanometric particles of Ni, which rearranged and formed small triangular arrays at sufficiently low applied overpotential. This particle pattern was induced by the ⟨111⟩ orientation and related to surface sensitivity of the nickel deposition in DES. The present work provides deep insights into the Ni electrodeposition mechanism in the selected deep eutectic solvent.

Keywords: AFM, Deep eutectic solvent, Glassy carbon, Nanostructures, Nickel electrodeposition, Platinum electrode, Pt(111), SEM, Surface sensitive


Zaffino, R. L., Mir, M., Samitier, J., (2017). Oligonucleotide probes functionalization of nanogap electrodes Electrophoresis , 38, (21), 2712-2720

Nanogap electrodes have attracted a lot of consideration as promising platform for molecular electronic and biomolecules detection. This is mainly for their higher aspect ratio, and because their electrical properties are easily accessed by current-voltage measurements. Nevertheless, application of standard current-voltages measurements used to characterize nanogap response, and/or to modify specific nanogap electrodes properties, represents an issue. Since the strength of electrical fields in nanoscaled devices can reach high values, even at low voltages. Here, we analyzed the effects induced by different methods of surface modification of nanogap electrodes, in test-voltage application, employed for the electrical detection of a desoxyribonucleic acid (DNA) target. Nanogap electrodes were functionalized with two antisymmetric oligo-probes designed to have 20 terminal bases complementary to the edges of the target, which after hybridization bridges the nanogap, closing the electrical circuit. Two methods of functionalization were studied for this purpose; a random self-assembling of a mixture of the two oligo-probes (OPs) used in the platform, and a selective method that controls the position of each OP at selected side of nanogap electrodes. We used for this aim, the electrophoretic effect induced on negatively charged probes by the application of an external direct current voltage. The results obtained with both functionalization methods where characterized and compared in terms of electrode surface covering, calculated by using voltammetry analysis. Moreover, we contrasted the electrical detection of a DNA target in the nanogap platform either in site-selective and in randomly assembled nanogap. According to our results, a denser, although not selective surface functionalization, is advantageous for such kind of applications.

Keywords: Biosensor bioelectronics, DNA electrophoresis, Nanogap electrodes, Self-assembled monolayers, Site-selective deposition


Arvizu-Rodríguez, L. E., Palacios-Padrós, A., Chalé-Lara, F., Fernández-Muñoz, J. L., Díez-Pérez, I., Sanz, F., Espinosa-Faller, F. J., Sandoval, J., Caballero-Briones, F., (2015). Phase and surface modification by electrochemical post deposition treatments in ultrasonic-assisted CuInSe2/Cu electrodeposited films Chalcogenide Letters , 12, (10), 537-545

CuInSe2 films were prepared onto Cu-cladded substrates by ultrasonic-assisted electrodeposition using different bath compositions and a fixed deposition potential of E=-1500 mV vs Ag/AgCl. In situ electrochemical treatments named selenization and electrocrystallization, in a Se4+ electrolyte were applied to modify the morphology, film structure and the phase composition. Films were characterized by scanning electron microscopy, X-ray diffraction, Raman spectroscopy and photocurrent response. A Cu2-xSe layer develops as the electrode is introduced into the electrolyte. The presence of Cu-In, In-Se, Cu-Se, cubic, hexagonal and tetragonal CuInSe2 phases as well as elemental In and Se was observed. After selenization, partial phase dissolution and Se deposition is observed and after the electrocrystallization treatment the secondary phases such as Cu-Se, Cu-In, In and Se reduce substantially and the grain sizes increase, as well as the photocurrent response. Phase diagrams are constructed for each set of films and reaction mechanisms are proposed to explain the phase evolution.

Keywords: CuInSe2, Electrodeposition, In situ electrochemical treatments, Phase composition, Surface modification


Azevedo, S., Diéguez, L., Carvalho, P., Carneiro, J. O., Teixeira, V., Martínez, Elena, Samitier, J., (2012). Deposition of ITO thin films onto PMMA substrates for waveguide based biosensing devices Journal of Nano Research , 17, 75-83

Biosensors' research filed has clearly been changing towards the production of multifunctional and innovative design concepts to address the needs related with sensitivity and selectivity of the devices. More recently, waveguide biosensors, that do not require any label procedure to detect biomolecules adsorbed on its surface, have been pointed out as one of the most promising technologies for the production of biosensing devices with enhanced performance. Moreover the combination of optical and electrochemical measurements through the integration of transparent and conducting oxides in the multilayer structures can greatly enhance the biosensors' sensitivity. Furthermore, the integration of polymeric substrates may bring powerful advantages in comparison with silicon based ones. The biosensors will have a lower production costs being possible to disposable them after use ("one use sensor chip"). This research work represents a preliminary study about the influence of substrate temperature on the overall properties of ITO thin films deposited by DC magnetron sputtering onto 0,5 mm thick PMMA sheets.

Keywords: ITO thin films, PMMA sheets, Waveguide biosensing devices, Biosensing devices, Conducting oxides, Dc magnetron sputtering, Electrochemical measurements, Enhanced performance, Innovative design, ITO thin films, Multilayer structures, Overall properties, PMMA sheets, Polymeric substrate, Production cost, Sensor chips, Silicon-based, Substrate temperature, Biosensors, Deposition, Design, Film preparation, Optical multilayers, Thin films, Vapor deposition, Waveguides, Substrates


Caballero-Briones, F., Palacios-Padrós, A., Sanz, Fausto, (2011). CuInSe2 films prepared by three step pulsed electrodeposition. Deposition mechanisms, optical and photoelectrochemical studies Electrochimica Acta , 56, (26), 9556-9567

p-Type semiconducting copper indium diselenide thin films have been prepared onto In2O3:Sn substrates by a recently developed pulse electrodeposition method that consists in repeated cycles of three potential application steps. The Cu–In–Se electrochemical system and the related single component electrolytes were studied by cyclic voltammetry to identify the electrode processes and study the deposition processes. In situ atomic force microscopy measurements during the first 100 deposition cycles denote a continuous nucleation and growth mechanism. Particles removed by film sonication from some of the films were characterized by transmission electron microscopy and determined to consist in nanoscopic and crystalline CuInSe2. The remaining film is still crystalline CuInSe2, as assessed by X-ray diffraction. The chemical characterization by combined X-ray photoelectron spectroscopy, X-ray fluorescence and inductively coupled plasma optical emission spectroscopy, showed that films were Cu-poor and Se-poor. Raman characterization of the as-grown films showed that film composition varies with film thickness; thinner films are Se-rich, while thicker ones have an increased Cu–Se content. Different optical absorption bands were identified by the analysis of the UV–NIR transmittance spectra that were related with the presence of CuInSe2, ordered vacancy compounds, Se, Cu2−xSe and In2Se3. The photoelectrochemical activity confirmed the p-type character and showed a better response for the films prepared with the pulse method.

Keywords: CuInSe2, Solar cells, Electrodeposition, Optical properties, As-deposited films, ITO substrate


Palacios-Padros, A., Caballero-Briones, F., Sanz, F., (2010). Enhancement in as-grown CuInSe2 film microstructure by a three potential pulsed electrodeposition method Electrochemistry Communications , 12, (8), 1025-1029

P-type copper indium diselenide (CuInSe2) films have been prepared onto ITO substrates by an electrodeposition method, that sequentially applies potential pulses at the deposition potential of each element Cu, Se and In, and then step it back in cyclically to induce the solid state reaction between the elements. Two electrolyte concentrations as well as three different pulse durations were assessed. The resulting films were compared with those deposited at fixed electrode potentials. As-grown films are nanocrystalline and have an E-g similar to 0.95 eV. Raman spectroscopy shows that Se and Cu-Se contents decrease while pulse duration increases and electrolyte concentration decreases. Cu-Se phases are even absent for films grown at the low electrolyte concentration. These results represent a great improvement in the film phase purity reducing the need of post-deposition treatments.

Keywords: CIS, Pulsed electrodeposition, Raman, Solar cells


Lagunas, A., Comelles, J., Martinez, E., Samitier, J., (2010). Universal chemical gradient platforms using poly(methyl methacrylate) based on the biotin streptavidin interaction for biological applications Langmuir , 26, (17), 14154-14161

This article describes a simple method for the construction of a universal surface chemical gradient platform based on the biotin streptavidin model. In this approach, surface chemical gradients were prepared in poly(methyl methacrylate) (PM MA), a biocompatible polymer, by a controlled hydrolysis procedure. The physicochemical properties of the resulting modified surfaces were extensively characterized. Chemical analysis carried out via time-of-flight secondary ion mass spectrometry (ToRSIMS) and X-ray photoelectron spectroscopy (XPS) showed the formation of a smooth, highly controllable carboxylic acid gradient of increasing concentration along the sample surface. Atomic force microscopy (AFM) and contact angle (CA) results indicate that, in contrast with most of the chemical gradient methods published in the literature, the chemical modification of the polymer surface barely affects its physical properties. The introduction of carboxylic acid functionality along the surface was then used for biomolecule anchoring. For this purpose, the surface was activated and derivatized first with biotin and finally with streptavidin (SA V) in a directed orientation fashion. The SAV gradient was qualitatively assessed by fluorescence microscopy analysis and quantified by surface plasmon resonance (SPR) in order to establish a quantitative relationship between SAV surface densities and the surface location. The usefulness of the fabrication method described for biological applications was tested by immobilizing biotinylated bradykinin onto the SAV gradient. This proof-of-concept application shows the effectiveness of the concentration range of the gradient because the effects of bradykinin on cell morphology were observed to increase gradually with increasing drug concentrations. The intrinsic characteristics of the fabricated gradient platform (absence of physicochemical modifications other than those due to the biomolecules included) allow us to attribute cell behavior unequivocally to the biomolecule surface density changes.

Keywords: Wettability gradient, Polyethylene surface, Combinatorial, Immobilization, Biomaterials, Fabrication, Deposition, Bradykinin, Monolayers, Discharge


Caballero-Briones, F., Palacios-Padros, A., Pena, J. L., Sanz, F., (2008). Phase tailored, potentiodynamically grown P-Cu2-xTe/Cu layers Electrochemistry Communications , 10, (11), 1684-1687

In this work we successfully prepared p-type semiconducting Cu2-xTe layers on Cu substrates by applying a potential multistep signal. Spontaneously deposited tellurium layers were reduced in a single cathodic sweep. The X-ray diffraction characterization showed the presence of single-phased, crystalline Cu2-xTe in the weissite form. A further anodization step allows crystallization of several phases such as CU1.75Te, Cu0.664Te0.336 and CU7Te4. This type of sample was found to be photoactive. The prepared films are p-type and have carrier concentrations in the order of 10(21) CM-3, suitable for CdTe-CU2-xTe contacts.

Keywords: Copper telluride, Electrochemical signal, XRD, Morphology, EIS, Photocurrent, Telluride thin-films, Solar cells, Deposition, Cu


Lopez, M. J., Caballero, D., Campo, E. M., Perez-Castillejos, R., Errachid, A., Esteve, J., Plaza, J. A., (2008). Focused ion beam-assisted technology in sub-picolitre micro-dispenser fabrication Journal of Micromechanics and Microengineering , 18, (7), 8

Novel medical and biological applications are driving increased interest in the fabrication of micropipette or micro-dispensers. Reduced volume samples and drug dosages are prime motivators in this effort. We have combined microfabrication technology with ion beam milling techniques to successfully produce cantilever-type polysilicon micro-dispensers with 3D enclosed microchannels. The microfabrication technology described here allows for the designing of nozzles with multiple shapes. The contribution of ion beam milling has had a large impact on the fabrication process and on further customizing shapes of nozzles and inlet ports. Functionalization tests were conducted to prove the viability of ion beam-fabricated micro-dispensers. Self-assembled monolayers were successfully formed when a gold surface was patterned with a thiol solution dispensed by the fabricated micro-dispensers.

Keywords: Dip-pen nanolithography, Silicon, Deposition, Microneedles, Delivery, Arrays, Polysilicon, Capillary, Systems, Gene


Manara, S., Paolucci, F., Palazzo, B., Marcaccio, M., Foresti, E., Tosi, G., Sabbatini, S., Sabatino, P., Altankov, G., Roveri, N., (2008). Electrochemically-assisted deposition of biomimetic hydroxyapatite-collagen coatings on titanium plate Inorganica Chimica Acta , 361, (6), 1634-1645

A biomimetic bone-like composite, made of self-assembled collagen fibrils and carbonate hydroxyapatite nanocrystals, has been performed by an electrochemically-assisted deposition on titanium plate. The electrolytic processes have been carried out using a single type I collagen molecules suspension in a diluted Ca(NO3)(2) and NH4H2PO4 solution at room temperature and applying a constant current for different periods of time. Using the same electrochemical conditions, carbonate hydroxyapatite nanocrystals or reconstituted collagen. brils coatings were obtained. The reconstituted collagen. brils, hydroxyapatite nanocrystals and collagen fibrils/apatite nanocrystals coatings have been characterized chemically, structurally and morphologically, as well as for their ability to bind fibronectin (FN). Fourier Transform Infrared microscopy has been used to map the topographic distribution of the coating components at different times of electrochemical deposition, allowing to single out the individual deposition steps. Moreover, roughness of Ti plate has been found to affect appreciably the nucleation region of the inorganic nanocrystals. Laser scanning confocal microscopy has been used to characterize the FN adsorption pattern on a synthetic biomimetic apatitic phase, which exhibits a higher affinity when it is inter-grown with the collagen fibrils. The results offer auspicious applications in the preparation of medical devices such as biomimetic bone-like composite-coated metallic implants.

Keywords: Hydroxyapatite-collagen coating, Electrochemically-assisted deposition, Micro-imaging FTIR spectroscopy, Laser scanning confocal microscopy, Biomimetic crystal growth, Fibronectin binding