Publications

by Keyword: LB films


By year:[ 2019 | 2018 | 2017 | 2016 | 2015 | 2014 | 2013 | 2012 | 2011 | 2010 | 2009 | 2008 | 2007 | 2006 | 2005 ]

Oncins, G., Torrent-Burgues, J., Sanz, F., (2008). Nanomechanical properties of arachidic acid Langmuir-Blodgett films Journal of Physical Chemistry C , 112, (6), 1967-1974

The nanomechanical properties of Langmuir-Blodgett monolayers of arachidic acid extracted at surface pressures of 1, 15, and 35 mN/m and deposited on mica were investigated by atomic force microscopy, force spectroscopy, and lateral force microscopy. It was experimentally demonstrated that the arachidic acid molecular orientation depends on the extraction pressure. According to this, tilting angles of 50, 34, and 22 degrees with respect to the surface perpendicular were detected and identified as conformations that maximize van der Waals interactions between the arachidic acid alkyl chains. The vertical force needed to puncture the monolayers with the AFM tip strongly depends on the molecular tilting angles attained at different monolayer extraction surface pressures, obtaining values that range from 13.07 +/- 3.24 nN for 50 degrees to 22.94 +/- 5.49 nN for 22 degrees tilting angles. The different molecular interactions involved in the monolayer cohesion are discussed and quantitatively related to the experimental monolayer breakthrough forces. The friction measurements performed from low vertical forces up to monolayer disruption reveal the existence of three well-defined regimes: first, a low friction response due to the elastic deformation of the monolayer, which is followed by a sharp increase in the friction force due to the onset of a sudden plastic deformation. The last regime corresponds to the monolayer rupture and the contact between tip and substrate. The friction coefficient of the substrate is seen to depend on the monolayer extraction pressure, a fact that is discussed in terms of the relationship between the sample compactness and its rupture mechanism.

Keywords: AFM, SAM, Reflection-absortion spectroscopy, Lipid-bilayers, Frictional-properies, Molecular-structure, Thermal behavior, Nanometer-scale, Chain-length, LB films


Guaus, E., Errachid, A., Torrent-Burgues, J., (2008). Voltammetric response of a glassy carbon electrode modified by a Langmuir-Blodgett film of a thiomacrocyclic compound Journal of Electroanalytical Chemistry , 614, (1-2), 73-82

A Langmuir-Blodgett (LB) film of a thiomacrocyclic (ThM) compound was deposited on the surface of a glassy carbon electrode (GCE) sheet, from a subphase containing Cu(II) ions. The study of the voltammetric response of this modified GCE when the ThM was bonded to Cu2+, showed that the films had the behaviour of confined species of an electrode surface, and that the current density of the voltammograms increased with the number of LB layers deposited. On the other hand, a LB film of the ThM compound was deposited on the surface of a GCE sheet from a subphase of pure water. When the voltammetric response of the GCE-ThM electrode was studied in a Cu2+-SO42- solution, it was found that a membrane model applies to describe the effect of the LB film on the GCE surface.

Keywords: Modified electrodes, Langmuir-Blodgett films, Cyclic voltammetry, Permeation at LB films, Membrane model of a thin film